The role of potassium in the corrosion of superheater materials in boilers firing biomass
Lehmusto, Juho (2013-12-13)
Tässä tietueessa ei ole tiedostoja, ainoastaan metadata.
Lehmusto, Juho
Åbo Akademi University, Process Chemistry Centre
13.12.2013
Julkaisu on tekijänoikeussäännösten alainen. Teosta voi lukea ja tulostaa henkilökohtaista käyttöä varten. Käyttö kaupallisiin tarkoituksiin on kielletty.
Tiivistelmä
Inhibition of global warming has become one of the major goals for the coming decades. A key strategy is to replace fossil fuels with more sustainable fuels, which has generated growing interest in the use of waste-derived fuels and of biomass fuels. However, from the chemical point of view, biomass is an inhomogeneous fuel, usually with a high concentration of water and considerable amounts of potassium and chlorine, all of which are known to affect the durability of superheater tubes. To slow down or reduce corrosion, power plants using biomass as fuel have been forced to operate at lower steam temperatures as compared to fossil fuel power plants. This reduces power production efficiency: every 10°C rise in the steam temperature results in an approximate increase of 2% in power production efficiency. More efficient ways to prevent corrosion are needed so that power plants using biomass and waste-derived fuels can operate at higher steam temperatures.
The aim of this work was to shed more light on the alkali-induced corrosion of superheater steels at elevated temperatures, focusing on potassium chloride, the alkali salt most frequently encountered in biomass combustion, and on potassium carbonate, another potassium salt occasionally found in fly ash. The mechanisms of the reactions between various corrosive compounds and steels were investigated.
Based on the results, the potassium-induced accelerated oxidation of chromia protected steels appears to occur in two consecutive stages. In the first, the protective chromium oxide layer is destroyed through a reaction with potassium leading to the formation of intermediates such as potassium chromate (K2CrO4) and depleting the chromium in the protective oxide layer. As the chromium is depleted, chromium from the bulk steel diffuses into the oxide layer to replenish it. In this stage, the ability of the material to withstand corrosion depends on the chromium content (which affects how long it takes the chromium in the oxide layer to be depleted) and on external factors such as temperature (which affects how fast the chromium diffuses into the protective oxide from the bulk steel). For accelerated oxidation to continue, the presence of chloride appears to be essential.
The aim of this work was to shed more light on the alkali-induced corrosion of superheater steels at elevated temperatures, focusing on potassium chloride, the alkali salt most frequently encountered in biomass combustion, and on potassium carbonate, another potassium salt occasionally found in fly ash. The mechanisms of the reactions between various corrosive compounds and steels were investigated.
Based on the results, the potassium-induced accelerated oxidation of chromia protected steels appears to occur in two consecutive stages. In the first, the protective chromium oxide layer is destroyed through a reaction with potassium leading to the formation of intermediates such as potassium chromate (K2CrO4) and depleting the chromium in the protective oxide layer. As the chromium is depleted, chromium from the bulk steel diffuses into the oxide layer to replenish it. In this stage, the ability of the material to withstand corrosion depends on the chromium content (which affects how long it takes the chromium in the oxide layer to be depleted) and on external factors such as temperature (which affects how fast the chromium diffuses into the protective oxide from the bulk steel). For accelerated oxidation to continue, the presence of chloride appears to be essential.